Microstructure and oxidation of a Ni–Al based intermetallic coating formation on a Monel-400 alloy

OpenAlex English

Abstract The purpose of this work was to examine how the microstructure and oxidation characteristics of Monel 400 Alloy were affected by the low-temperature aluminizing method. Monel 400 alloy was subjected to a low-temperature aluminizing procedure for 2 and 4 h at 600, 650, and 700 °C. Pure aluminum powder was used as the source of aluminum deposition to prepare the packs for the process. The activator and inert filler utilized were ammonium chloride (NH4Cl) and Al2O3 powder, respectively. The coating surfaces were characterized using energy dispersive spectroscopy (EDS) and scanning electron microscopy (SEM), as well as X-ray diffraction (XRD) analysis. It was discovered that the through-thickness variance in the layer microstructure varied between 4 and 30 µm, and that it increased with greater process temperatures and times. The coating layer hardness grew to 800 HV after the deposition process, whereas the matrix hardness remained at 200 HVN. Furthermore, the sample that was coated at 600 °C for 4 h was exposed to oxidation at 750–800 and 850 °C. It was found that the oxidation kinetics were 176 kJ/mol.