High-Speed Ultraviolet Photodetector Based on p-GaN Gate HEMT for Flame Monitoring

OpenAlex İngilizce

The p-GaN gate high electron mobility transistor (HEMT) with a$2.0\times 10^{-{5}}$cm2 sensitive area as a UV photodetector (PD) has been designed and fabricated in this study. AlGaN/gallium nitride (GaN) heterostructure was adopted to get a 2-D electron gas (2DEG) as a conductive channel, resulting in a high photoresponsivity of$8.07\times 10^{{4}}$A/W, a sharp cutoff wavelength at 360 nm, high UV-to-visible rejection ratio of$1.80\times 10^{{6}}$, rise and decay time of 0.12 and 1.0 ms, respectively. The dark current of$5.44\times 10^{-{7}}$A, the photocurrent of$4.42\times 10^{-{3}}$A at 5 V, the external quantum efficiency (EQE) of 2.77%$\times 10^{{5}}$%, and the detectivity of$8.31\times 10^{{14}}$Jones for the UV PD were determined under a low UV light intensity of 5 mW/cm2 at 360-nm UV illumination. The obtained results show that the performance of as-fabricated UV PD based on AlGaN/GaN HEMT is significantly improved compared to the literature. This device, which has lower noise equivalent power (NEP) and enhanced detectivity features compared to existing ones, is a promising candidate for military and space applications.