An HBS@GaSe:Dy-Based Organic/Inorganic Hybrid Heterojunction for High-Performance Multicolor Photodetectors
ACS Applied Electronic Materials
- Yıl
- 2025
- ISSN
2637-6113- Tür
- article
Veri kaynağı ayrımı
- YÖKSİS YÖKSİS makale kaydı
- OpenAlex OpenAlex zenginleştirmesi (özet, atıf, konular)
Özet
İngilizce (OpenAlex)
Herein, a multicolor heterojunction photodetector was fabricated using organic Hibiscus sabdariffa (HBS) material and two-dimensional (2D) dysprosium-doped GaSe as an HBS@GaSe design. For the fabricated hybrid heterojunction, multicolor broadband photodetection covering UV–vis–NIR spectra is observed for the light power density of 7 mW/cm 2, and the optoelectronic properties of the heterojunction photodetector were studied in detail. Electrooptical measurements were performed with I – V measurements under white light as well as under 365 nm violet (UV), 590 nm (yellow), and 850 nm IR light irradiation. For this purpose, the key parameters of a photodetector, such as ON/OFF ratio, responsivity, specific detectivity, NPDR, NEP, and EQE, have been calculated. Under illumination of 590 nm, a maximum ON/OFF ratio of 1.8 × 10 4 was observed for −1.76 V reverse bias. The photodetectors exhibit excellent photoresponse properties, with a high responsivity of 2166 mA/W, an EQE of 736%, and a high detectivity of 6.81 × 10 12 Jones at 590 nm. The high responsivity was attributed to the interfacial traps, enhancing the photoconductivity gain. Our work suggests that the HBS@GaSe-based organic/inorganic hybrid heterojunction is a promising candidate for ultrasensitive multicolor photodetection.
Konular
- Perovskite Materials and Applications
- 2D Materials and Applications
- Chalcogenide Semiconductor Thin Films
Birincil konu Perovskite Materials and Applications