Templated Grain Growth of Textured Piezoelectric Ceramics
- Yıl
- 2004
- Tür
- article
Veri kaynağı ayrımı
- YÖKSİS YÖKSİS makale kaydı
- YÖKSİS dergi adı Critical Reviews in Solid State and Materials Sciences
- Katalog eşleşmesi (ISSN) Critical Reviews in Solid State and Materials Sciences
- OpenAlex OpenAlex zenginleştirmesi (özet, atıf, konular)
Özet
OpenAlex · İngilizce
Crystallographic texturing of polycrystalline ferroelectric ceramics offers a means of achieving significant enhancements in the piezoelectric response. Templated grain growth (TGG) enables the fabrication of textured ceramics with single crystal-like properties, as well as single crystals. In TGG, nucleation and growth of the desired crystal on aligned single crystal template particles results in an increased fraction of oriented material with heating. To facilitate alignment during forming, template particles must be anisometric in shape. To serve as the preferred sites for epitaxy and subsequent oriented growth of the matrix, the template particles need to be single crystal and chemically stable up to the growth temperature. Besides templating the growth process, the template particles may also serve as seed sites for phase formation of a reactive matrix. This process, referred to as Reactive TGG (RTGG), has been used to obtain highly oriented Pb(Mg1/3Nb2/3)O3-PbTiO3, Sr0.53Ba0.47Nb2O6, and (Na1/2Bi1/2)TiO3-BaTiO3. Highly oriented Bi4Ti3O12, Sr2Nb2O7, CaBi4Ti4O15, Pb(Mg1/3Nb2/3)O3-PbTiO3, Sr0.53Ba0.47Nb2O6 and (Na1/2Bi1/2)TiO3-BaTiO3 ceramics have been produced by TGG. The resulting ceramics show texture levels up to 90%, and significant enhancements in the piezoelectric properties relative to randomly oriented ceramics with comparable densities. For example, piezoelectric coefficients of textured piezoelectrics are from 2 to 3 times higher than polycrystalline ceramics and as high as 90% of the single crystal values. In textured PMN-PT, a low field (< 5 kV/cm) piezoelectric coefficient (d 33) of ∼1600 pC/N was obtained with > 0.3% strain (at 50 kV/cm). The high field dielectric and electromechanical properties of textured perovskites are more hysteretic than those of single crystals, probably as a result of clamping by the residual template particles, residual random grains, the presence of non-ferroelectric second phases, and a wide orientation distribution. Lateral clamping of one grain by another may also be an important factor in fiber-textured samples. Means to further improve the quality of texture and thus properties of textured piezoelectric ceramics by TGG are presented.
Konular
Atıflar
OpenAlex cited_by_count. WoS veya Scopus atıf sayısı değildir; o kaynaklar için ayrı kolon yoktur.
617 atıf
OpenAlex cited_by_count (önbellek / veritabanı)
Yerel katalogda bu makaleye atıf yapan 59 yayın (OpenAlex referans eşleşmesi; tam dünya listesi değildir).
- Textured PMN PT and PMN PZT 2008
- Microstructural Features and Electrical Properties of Copper Oxide Added Potassium Sodium Niobate Ceramics 2010
- Thermoelectric power factor enhancement of textured ferroelectric SrxBa1–xNb2O6–δceramics 2011
- Hydrothermal Synthesis 2020
- Fundamental limitation to the magnitude of piezoelectric response of ⟨001⟩pc textured K0.5Na0.5NbO3 ceramic 2014
- Enhancement of electrical properties in the ternary PMN–PT–PZ through compositional variation, crystallographic texture, and quenching 2020
- Processing and mechanical properties of textured mullite/zirconia composites 2006
- High strain 001 textured Pb Mg1 3Nb2 3 O3 Pb Yb1 2Nb1 2 O3 PbTiO3 piezoelectric ceramics 2016
- Processing and ferroelectric behavior of textured KSr2Nb5O15 ceramics 2006
- Processing and Properties of Textured Potassium Strontium Niobate KSr2Nb5O15 Ceramic Fibers Texture Development 2012