Effect of Fiber Content on Failure Modes of Glass Fiber Reinforced Injection Molded Polyamide 66 Composites
Veri kaynağı ayrımı
- YÖKSİSYÖKSİS makale kaydı
- YÖKSİS dergi adıAdvanced Materials Research
- Katalog eşleşmesi (ISSN)Advanced Materials Research (discontinued)
- OpenAlexOpenAlex zenginleştirmesi (özet, atıf, konular)
- Semantic Scholaratıf sayısı (OpenAlex ile birleştirilmez)
Özet
In the present study, glass fiber reinforced Polyamide 66 composites were produced using laboratory type twin screw extrusion and injection molding processes. The glass fiber reinforcement was applied at 1, 10, 15, 20, 25 and 30 wt% loadings. The morphological structure of the samples and failure modes of glass fiber reinforced Polyamide 66 composites were investigated using scanning electron microscopy (SEM) analysis on fractured surfaces of tensile tested samples in this study.
Konular
Atıflar
OpenAlex cited_by_count. WoS veya Scopus atıf sayısı değildir; o kaynaklar için ayrı kolon yoktur.
2atıfOpenAlex · cited_by_count (önbellek / veritabanı)
Yerel katalogda bu makaleye atıf yapan 2 yayın (OpenAlex referans eşleşmesi; tam dünya listesi değildir).